| Aluminum Silicate, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...Vea Mas Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. Vea Menos | |
| Calcium Carbonate, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...Vea Mas Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm/ gauge 7+ NS. Vea Menos | |
| Gloss Lacquer Formula for Airless Spray Application (Formulation #07-1019B) | Ashland | Un spray sin aire basado en Neocryl* XK98 acrílico barniz brillante. | |
| Gloss Parquet Lacquer (Formulation #07-1020A) | Ashland | Un barniz de parquet brilloso basado en copolímero de uretano/acrílico Neopac* E106. | |
| High Build Exterior Masonry Coating (Formulation #07-1040B) | Ashland | PVC 50% - Pliotec LEB 18* low exudation binder exterior masonry coating. | |
| High Gloss White Coat Paint (Formulation #07-1021B) | Ashland | PVC 20%-Synaqua* 4804 capa superior blanca de alto brillo emulsión alquídica con Aquaflow™ NLS-205 y Aquaflow™ NMS-450 modificadores de reología. | |
| High Gloss White Top Coat - Higher Solids (Formulation #07-1022B) | Ashland | PVC 20%-Uradil* AZ 785-Z52 capa superior blanca de alto brillo emulsión alquídica con Aquaflow™ NMS-450 y Aquaflow™ NHS-300 modificadores de reología. | |
| High Gloss White Top Coat (Formulation #07-1023B) | Ashland | PVC 19%-Primal* HG 74D pintura blanca de alto brillo acrílico con Aquaflow™ NMS-450 y Aquaflow™ NHS-350 modificadores de reología. | |
| High Gloss White Top Coat (Formulation #07-1024B) | Ashland | PVC 19%-Primal* HG 74D-pintura blanca de alto brillo acrílico con Aquaflow™ XLS-500 y Aquaflow™ NHS-300 modificadores de reología. | |
| High Gloss White Top Coat (Formulation #07-1025B) | Ashland | PVC 20%-Uradil* AZ 785-Z52 capa superior blanca de alto brillo emulsión alquídica con Aquaflow™ XLS-530 y Aquaflow™ NMS-450 modificadores de reología. | |
| High Gloss White Top Coat (Formulation #07-1030B) | Ashland | Esta formulación se utiliza para la pintura de alto brillo y blanca de alto brillo. Utiliza Aquaflow™ NMS-450, Aquaflow™ NHS-350, BIC Nuosept™ y Dextrol™ OC 180. | |
| Interior / Exterior Deeptone Semi Gloss Paint (Formulation #07-1018B) | Ashland | PVC 43%-Acronal* S-559 Deeptone estireno acrílico pintura semi-brillante con Aquaflow™ XLS-500 y Aquaflow™ NHS-300 modificadores de reología. | |
| Interior / Exterior Semi Gloss Paint (Formulation #07-1031B) | Ashland | PVC 30%-Neocryl* pintura blanca XK-90 acrílico semi-brillante con Aquaflow™ XLS-500 y Aquaflow™ NHS-300 modificadores de reología | |
| Interior / Exterior Semi Matt Paint (Formulation #07-1034A) | Ashland | PVC 38%-Acronal* S 559 pintura blanca semi-mate de interior de vinilo de etileno con Natrosol™ HE 3KB hidroxietilcelulosa modificada hidrófobamente (HMHEC) y Aquaflow™ NMS-450 modificador de reología. | |
| Interior / Exterior Semi Matt Paint (Formulation #07-1035A) | Ashland | PVC 38%-Mowilith* LDM 1871 pintura blanca semi-mate de interior de vinilo de etileno acetato con Natrosol™ HE 3KB hidroxietilcelulosa modificada hidrófobamente (HMHEC). | |
| Interior / Exterior Semi-Gloss Paint (Formulation #07-1032B) | Ashland | PVC 30%-Neocryl* pintura blanca XK-90 acrílico semi-brillante con Aquaflow™ XLS-530 y Aquaflow™ NHS-350 modificadores de reología. | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1033B) | Ashland | PVC 38%-Mowilith* LDM 1871 pintura blanca semi-mate de interior de vinilo de etileno con Natrosol Plus™ 330 hidroxietilcelulosa modificada hidrófobamente (HMHEC) y Aquaflow™ NMS-450 modificador de reología. | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1036B) | Ashland | PVC 38%-Alberdingk* AS 6002 pintura blanca semi-mate de interior de vinilo de etileno con Natrosol™ 330 hidroxietilcelulosa modificada hidrófobamente (HMHEC). | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1037B) | Ashland | PVC 38%-Vinnapas* EZ 3010 pintura blanca semi-mate de interior de vinilo de etileno con Natrosol Plus™ 330 hidroxietilcelulosa modificada hidrófobamente (HMHEC). | |
| Interior Flat Paint Formula with 2% Titanium Dioxide Pigment (Formulation #07-1043) | Ashland | This formulation is based on PVC 85% and Acronal* 290D. | |
| Interior Flat Paint Formula with 2% Titanium Dioxide Pigment (Formulation #07-1044A) | Ashland | PVC 85% - Acronal* S790 Styrene Acrylic Interior Flat White Paint with 2% pigment. | |
| Interior Flat Paint (Formulation #07-1012B) | Ashland | PVC 70% - Acronal S559* styrene acrylic interior flat white paint. | |
| Interior Flat Paint (Formulation #07-1013A) | Ashland | PVC 75%-Acronal* 290D pintura blanca mate de interior estireno acrílico con Natrosol Plus™ 330. | |
| Interior Flat Paint (Formulation #07-1014A) | Ashland | PVC 85%-Acronal* 290D pintura blanca mate de interior estireno acrílico con Natrosol™ 250 HHBR. | |
| Interior Flat Paint (Formulation #07-1015C) | Ashland | PVC 70%-Mowilith* LDM 1871 pintura blanca mate de interior acetato de vinilo de etileno con Natrosol Plus™ 330 y Aquaflow™ NHS-300. | |
| Interior Flat Paint (Formulation #07-1016B) | Ashland | PVC 70%-Mowilith* LDM 1871 pintura blanca mate de interior acetato de vinilo de etileno con Natrosol Plus™ 330 y Aquaflow™ NMS-450. | |
| Interior Flat Paint (Formulation #07-1017A) | Ashland | PVC 70% - Mowilith LDM 1871* vinyl acetate ethylene interior flat white paint. | |
| Interior Flat Paint (Formulation #07-1026A) | Ashland | PVC 80%- Acronal* S 559 pintura blanca mate de interior estireno acrílico con Natrosol™ HE 3KB y Aquaflow™ NHS-350 modificadores de reología. | |
| Interior Flat Paint (Formulation #07-1027A) | Ashland | PVC 85% - Acronal 290D* styrene acrylic interior flat white paint. | |
| Interior Flat Paint (Formulation #07-1028B) | Ashland | PVC 70%-Mowilith * LDM 1871 pintura blanca mate de interior acetato de vinilo de etileno con Natrosol™ 250 HHBR hidroxietilcelulosa (HEC). | |
| Interior Flat Vinyl Acrylic Dry TiO2 | Ashland | TiO2 (dióxido de titanio). | |
| Interior Flat Vinyl Acrylic TiO2 Slurry | Ashland | Vinilo Acrílico Mate Interior TiO2 (dióxido de titanio) solución. | |
| Interior Satin Acrylic TiO2 Slurry | Ashland | Satinado Acrílico Interior TiO2 (dióxido de titanio) solución. | |
| Interior Semi-Gloss Acrylic TiO2 Slurry | Ashland | Acrílicor Semi-Brillo Interior TiO2 (dióxido de titanio) solución. | |
| Interior/Exterior Gloss Acrylic Dry TiO2 | Ashland | Acrpilico Seco Brilloso Interior/Exterior TiO2 (dióxido de titanio). | |
| Interior/Exterior Gloss Paint (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...Vea Mas Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved- 7+ NS/ <10 μm. Vea Menos | |
| Interior/Exterior Matt Paint (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...Vea Mas Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. 5+ NS/ min. of 20 μm. Vea Menos | |
| Interior/Exterior Semi Glossy Paint Waterborne Coatings (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...Vea Mas Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. -7 NS/ min. of 15 μm. Vea Menos | |
| Interior/Exterior Semi-Matt Paint (Formulation #07-1039B) | Ashland | Esta formulación es para pintura semi-mate interior/exterior que utiliza los productos Aquaflow™ NHS-350 y Aquaflow™ NLS-220 como espesantes asociativos sintéticos no iónicos. | |
| Solventborne 2K PU White Topcoat (Formulation #21-20001) | Patcham USA | This solventborne 2K PU white topcoat features Pat-Add DA 1801. It is suitable for general industrial coatings, wood coatings, and auto refinish coatings. | |
| Talc, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...Vea Mas Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. Vea Menos | |
| Top Protection Coat (Formulation #07-1038A) | Ashland | Una capa de protección superior basada en Aquaflow™ NLS 200 modificador de reología. | |
| Waterborne Epoxy Primer (Formulation #21- 10001) | Patcham USA | This waterborne epoxy primer features Pat-Add DA 817. It is suitable for general industrial coatings. | |
| White Acrylic Topcoat for Airless Spray (Formulation #07-1041A) | Ashland | PVC 13% based on Neocryl* XK-98 acrylic topcoat - airless and air sprayable. | |
| White Acrylic Topcoat for Airmix Spray (Formulation #07-1029B) | Ashland | Una capa superior acrílica blanca sistema airmix rociable con Aquaflow™ XLS-525 y Aquaflow™ XLS-550 no iónico espesante asociativo sintético (NSAT). | |
| White Anti-Corrosive Primer for Airless Spray (Formulation #07-1042A) | Ashland | Based on Neocryl* XK-87 and Nubirox* 106, primer - airless and air sprayable. | |
| Zinc Oxide, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...Vea Mas Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. Vea Menos |